I-Corundum mullite refractory castable luhlobo lwamandla aphezulu angamiliselwanga izinto ezi refractory ezithengiswa kwi RS Company, ezinokusetyenziswa kwiziko lesamente. I-Corundum mullite castables inokwenza iipropathi eziphezulu ezifana namandla aphezulu okutyumza, ukuzinza kobushushu obuphezulu, ukuxhathisa ukutshatyalaliswa kwe-thermal, ukunxiba kunye nokumelana nokukhukuliseka kweekhemikhali kwi-lining ye-boiler yesikhululo samandla amakhulu kunye nezinye izixhobo zokushisa eziphezulu. i-refractory corundum mullite castable ingasetyenziswa kwiziko lensimbi, i-sement kiln, i-glass furnace, i-iron eyenza i-oven, i-ceramic tunnel kiln njalo njalo.
Izinto eziphambili zezinto ezibonakalayo ze-corundum mullite ezichithwayo yi-aluminiyam oxide aggregate, umgangatho ophezulu ococekileyo wendalo we-mullite ore, kunye ne-calcium aluminate samente njenge-agent edibeneyo. icorundum mullite refractory castable yenziwa ngokutshiswa kobushushu obuphezulu sisithando somlilo esiphambili. I-corundum mullite amandla aguquguqukayo kunye namandla oxinzelelo ayanda kuqala kwaye anciphe ngoko ngokunyuka kobushushu bonyango lobushushu. Kwaye xa umxholo wamandla we-alumina yi-5%, amandla e-flexural afikelela phezulu.
Umxholo we-Al2O3 ungaphezulu kwe-90%, kunye ne-corundum mullite insulation castable kunye ne-corundum njengesigaba esiphambili se-crystal sixutywe kunye ne-dispersants efanelekileyo, i-coagulants, i-fibers yensimbi engenasici, edityaniswe ngokwendlela engqongqo. I-refractory corundum mullite castable ineempawu ezininzi, ezifana namandla aphezulu okushisa, ukuxhathisa ukunxiba kunye nokuchasana nokutshatyalaliswa, ukushisa okuphezulu, ukuxhathisa ukutshatyalaliswa kobushushu, ukunyanzeliswa kwe-corrosion, ukutywinwa kakuhle kunye nokuxinana kwangaphambili.
Into | NM-1 | NM-2 | NM-3 |
Al2O3 % ≥ | 75 | 80 | 85 |
CaO % ≤ | 2 | 2 | 2 |
Ubuninzi bobuninzi g/cm3 > | 2.75 | 2.8 | 2.9 |
Amandla okutyumza iMpa(1400℃, 3h) | >95 | >105 | >110 |
Imodyuli yokugqabhuka iMpa(1400℃, 3h) | >13.5 | >15.0 | >16.0 |
Ilahleko yeqondo lobushushu begumbi cm3 | <8.5 | <7.3 | <6 |
0.2MPa, refractoriness phantsi komthwalo ukuqala ubushushu ℃ | >1490 | >1530 | >1560 |
Ukumelana nokothuka kwe-Thermal (900℃, ukupholisa kwamanzi)/amaxesha | >20 | >20 | >20 |
Max. ubushushu bokusebenza ℃ | 1550 | 1600 | 1600 |
Ukufudumeza umyinge wotshintsho % | <-0.3 | <-0.2 | <-0.2 |
<-0.2